Ni(OH){sub 2} nanoflakes electrodeposited on Ni foam-supported vertically oriented graphene nanosheets for application in asymmetric supercapacitors
Highlights: • Ni(OH){sub 2}/vertically oriented graphene nanosheets (V-GNs) was prepared. • Ni(OH){sub 2}/V-GNs had enhanced specific capacitance, cycling reversibility and stability. • Performance of Ni(OH){sub 2}/GNs/NF-AC asymmetric supercapacitor was studied. - Abstract: Binderless Ni(OH){sub 2} nanoflakes grown on Ni foam (NF)-supported vertically oriented graphene nanosheets (V-GNs) has been fabricated as a positive electrode material for asymmetric supercapacitor (ASC), coupled with activated carbon (AC) as a counter electrode material. The introduction of V-GNs leads to dense growth of nanocrystalline β-Ni(OH){sub 2} that is confirmed by X-ray diffraction, transmission electron microscopic and scanning electron microscopic analyses. The electrochemical performances of the Ni(OH){sub 2}/GNs/NF electrode are characterized by cyclic voltammetry and charge–discharge tests, which exhibit high specific capacitance of 2215 F g{sup −1} at a scan current density of 2.3 A g{sup −1}, enhanced cycling stability and high rate capability. The Ni(OH){sub 2}/GNs/NF-AC-based ASC can achieve a cell voltage of 1.4 V and a specific energy density of 11.11 Wh kg{sup −1} at 0.5 mA cm{sup −2} with a nearly 100% coulombic efficiency at room temperature.
- OSTI ID:
- 22345261
- Journal Information:
- Materials Research Bulletin, Vol. 52; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis of MnO{sub 2}-graphene composites with enhanced supercapacitive performance via pulse electrodeposition under supergravity field
High-Performance Flexible All-Solid-State Asymmetric Supercapacitors Based on Vertically Aligned CuSe@Co(OH)2 Nanosheet Arrays