Controlling the size and optical properties of ZnO nanoparticles by capping with SiO{sub 2}
Graphical abstract: - Highlights: • Small and uniform sized ZnO nanoparticles were obtained with SiO{sub 2} coating. • ZnO and ZnO–SiO{sub 2} nanocomposite exhibited excitation wavelength dependent PL. • Maximum UV emission intensity was obtained with 353 nm excitation wavelength. • Excitation processes in SiO{sub 2} were also contributed to the UV intensity. • It was found that oxygen vacancies and interstitials enhanced with SiO{sub 2} coating. - Abstract: The size and shape of the ZnO nanoparticles synthesized through sol–gel method were controlled by capping with SiO{sub 2}. X-ray diffraction (XRD) and field emission scanning electron microscope (FE-SEM) and High Resolution Transmission Electron Microscope (HR-TEM) results demonstrated that the particle growth of the ZnO nanoparticles has been restricted to 5 nm with SiO{sub 2} capping. As a result, the absorption spectra of ZnO nanoparticles capped with SiO{sub 2} got blue shifted (toward lower wavelength side) due to strong quantum confinement effects. BET (Brunauer–Emmet–Teller) surface area pore size analyzer results showed that surface area of samples increased monotonously with increase of SiO{sub 2} concentration. It was observed that the absorption spectra of ZnO capped with SiO{sub 2} broadened with increase of SiO{sub 2} concentration. Absorption and photoluminescence excitation results (PLE) confirmed that this broadening is due to the absorption of non-bridging oxygen hole centers (NBOHC) of SiO{sub 2}. These results also indicated that ZnO nanoparticles capped with SiO{sub 2} are insensitive to Raman scattering. Maximum UV emission intensity was achieved with 353 nm excitation wavelength compared to 320 nm in ZnO as well as in SiO{sub 2} capped ZnO nanoparticles. Furthermore, there is an enhancement in the intensities of emission peaks related to oxygen vacancies and interstitials with SiO{sub 2} capping. The enhancement in the UV intensity is attributed to the surface passivation of ZnO nanoparticles and excitation processes in SiO{sub 2}.
- OSTI ID:
- 22341862
- Journal Information:
- Materials Research Bulletin, Vol. 49; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and optical investigations of oxygen defects in zinc oxide nanoparticles
Size-dependent structural phase transitions and their correlation with photoluminescence and optical absorption behavior of annealed Zn0.45Cd0.55S quantum dots
Related Subjects
37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION
ABSORPTION SPECTRA
EXCITATION
FIELD EMISSION
INTERSTITIALS
NANOPARTICLES
NANOSTRUCTURES
OPTICAL PROPERTIES
OXYGEN
PEAKS
PHOTOLUMINESCENCE
SCANNING ELECTRON MICROSCOPY
SILICA
SILICON OXIDES
SOL-GEL PROCESS
SURFACE AREA
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
ZINC OXIDES