Mechanical properties of Al-Cu alloy-SiC composites
Journal Article
·
· AIP Conference Proceedings
- Jurusan Fisika, FMIPA Universitas Negeri Jakarta, 13220 (Indonesia)
- PPS Ilmu Material, Department Fisika, FMIPA, Universitas Indonesia (Indonesia)
The synthesis of aluminum (Al) alloys, Al-Cu, from mixture 96.2 % Al and 3.8 % Cu has been prepared by melting process at a temperature of 1200°C. The adding 12.5 wt% up to 20 wt% of SiC on Al-Cu alloys samples has been investigated. The structure analyses were examined by X-Ray Diffractometer (XRD) and scanning electron microscope (SEM). Moreover, the morphology of Al-Cu alloys has been seen as structure in micrometer range. The hardness was measured by hardness Vickers method. According to the results, it can be assumed that the 15 wt% of SiC content is prefer content to get better quality of back to back hardness Vickers of Al-Cu alloys.
- OSTI ID:
- 22307895
- Journal Information:
- AIP Conference Proceedings, Vol. 1617, Issue 1; Conference: ICTAP 2013: 3. international conference on theoretical and applied physics, Malang, East Java (Indonesia), 10-11 Oct 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Age-hardening behavior of Al-Cu-SiC[sub p] composites synthesized by casting route
Development of Pore-Free Ti-Si-C MAX/Al-Si Composite Materials Manufactured by Squeeze Casting Infiltration
Effect of magnesium on the aging behavior of Al-Zn-Mg-Cu/Al{sub 2}O{sub 3} metal matrix composites
Journal Article
·
Wed Mar 01 00:00:00 EST 1995
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:22307895
Development of Pore-Free Ti-Si-C MAX/Al-Si Composite Materials Manufactured by Squeeze Casting Infiltration
Journal Article
·
Tue Oct 15 00:00:00 EDT 2019
· Journal of Materials Engineering and Performance
·
OSTI ID:22307895
+2 more
Effect of magnesium on the aging behavior of Al-Zn-Mg-Cu/Al{sub 2}O{sub 3} metal matrix composites
Journal Article
·
Mon Jul 01 00:00:00 EDT 1996
· Metallurgical Transactions, A
·
OSTI ID:22307895