Icosahedral quasicrystalline (Ti₁.₆V₀.₄Ni)₁₀₀₋xScx alloys: Synthesis, structure and their application in Ni-MH batteries
- Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, Yunnan (China)
- State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, CAS, Changchun 130022, Jilin (China)
Thanks to the revolutionary discovery of 5-fold symmetry contributed by Shechtman, quasicrystal is now recognized as another solid-state existing form. As the second largest class of quasicrystals, titanium-based icosahedral quasicrystals are very promising for hydrogen storage applications owing to their inherent abundant interstitial sites and favorable hydrogen-metal chemistry. In this context, (Ti₁.₆V₀.₄Ni)₁₀₀₋xScx (x=0.5–6) quaternary icosahedral quasicrystals have been successfully synthesized via arc-melting and subsequent melt-spinning techniques, and then their electrochemical performance toward hydrogen is explored. When the molar ratio of Sc addition is under 1%, a maximum discharge capacity of about 270 mA h g⁻¹ can be delivered. With further increasing Sc amount to 6%, good cycling stability as well as significantly retarded self-discharge rate (capacity retention 94% after 24 h relaxation) is observed. But meanwhile, the discharge capacities fall into 250-240 mA h g⁻¹, and the electrocatalytic activity improvement is highly demanded. - Graphical abstract: Quasicrystalline Ti–V–Ni–Sc hydrogen storage materials: Sc addition into Ti₁.₆V₀.₄Ni alloy forms the icosahedral phase (see picture). With optimal Sc dosage, the anodic cycling stability and self-discharge property are greatly enhanced. - Highlights: • Crystalline disallowed 5-fold symmetry is present in (Ti₁.₆V₀.₄Ni)₁₀₀₋xScx alloys. • Ti-based metastable quasicrystalline alloys can store hydrogen electrochemically. • A maximum discharge capacity of 270 mA h g⁻¹ can be delivered. • Advantageous cycle stability and self-discharge property benefit from Sc addition. • Ti and V dissolution is suppressed by an oxide layer resulting from Sc corrosion.
- OSTI ID:
- 22306349
- Journal Information:
- Journal of Solid State Chemistry, Vol. 202; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigations of the Electronic Properties and Surface Structures of Aluminium-Rich Quasicrystalline Alloys
High Voltage Operation of Ni‐Rich NMC Cathodes Enabled by Stable Electrode/Electrolyte Interphases