KNN–NTK composite lead-free piezoelectric ceramic
- NGK SPARK PLUG Co., Ltd., 2808 Iwasaki, Komaki, Aichi 485-8510 (Japan)
A (K,Na)NbO₃-based lead-free piezoelectric ceramic was successfully densified. It exhibited an enhanced electromechanical coupling factor of kₚ=0.52, a piezoelectric constant d₃₃=252 pC/N, and a frequency constant Nₚ=3170 Hz m because of the incorporation of an elaborate secondary phase composed primarily of KTiNbO₅. The ceramic's nominal composition was 0.92K₀.₄₂Na₀.₄₄Ca₀.₀₄Li₀.₀₂Nb₀.₈₅O₃–0.047K₀.₈₅Ti₀.₈₅Nb₁.₁₅O₅–0.023BaZrO₃ –0.0017Co₃O₄–0.002Fe₂O₃–0.005ZnO, abbreviated herein as KNN–NTK composite. The KNN–NTK ceramic exhibited a dense microstructure with few microvoids which significantly degraded its piezoelectric properties. Elemental maps recorded using transmission electron microscopy with energy-dispersive X-ray spectroscopy (TEM–EDS) revealed regions of high concentrations of Co and Zn inside the NTK phase. In addition, X-ray diffraction patterns confirmed that a small portion of the NTK phase was converted into K₂(Ti,Nb,Co,Zn)₆O₁₃ or CoZnTiO₄ by a possible reaction between Co and Zn solutes and the NTK phase during a programmed sintering schedule. TEM studies also clarified a distortion around the KNN/NTK interfaces. Such an NTK phase filled voids between KNN particles, resulting in an improved chemical stability of the KNN ceramic. The manufacturing process was subsequently scaled to 100 kg per batch for granulated ceramic powder using a spray-drying technique. The properties of the KNN–NTK composite ceramic produced using the scaled-up method were confirmed to be identical to those of the ceramic prepared by conventional solid-state reaction sintering. Consequently, slight changes in the NTK phase composition and the distortion around the KNN/NTK interfaces affected the KNN–NTK composite ceramic's piezoelectric characteristics.
- OSTI ID:
- 22305835
- Journal Information:
- Journal of Applied Physics, Vol. 116, Issue 15; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Publisher:
- American Institute of Physics (AIP)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Piezoelectric properties of (K{sub 0.5}Na{sub 0.5})(Nb{sub 1-x}Ta{sub x})O{sub 3}-K{sub 5.4}CuTa{sub 10}O{sub 29} ceramics
Piezoelectric properties of Li- and Ta-modified (K{sub 0.5}Na{sub 0.5})NbO{sub 3} ceramics
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BARIUM COMPOUNDS
CALCIUM COMPOUNDS
CERAMICS
COBALT OXIDES
INTERFACES
IRON OXIDES
LITHIUM COMPOUNDS
MICROSTRUCTURE
NIOBATES
PIEZOELECTRICITY
POTASSIUM COMPOUNDS
POWDERS
SINTERING
SODIUM COMPOUNDS
TITANIUM COMPOUNDS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
X-RAY SPECTROSCOPY
ZINC OXIDES
ZIRCONATES