Title: Investigation of chemical composition and crystal structure in sintered Ce{sub 15}Nd{sub 15}Fe{sub bal}B{sub 1} magnet

The substitution of cerium, a more abundant rare-earth element, for sintered Nd-Fe-B magnets has drawn intense interest. In the present work, nominal composition of Ce{sub 15}Nd{sub 15}Fe{sub bal}B{sub 1} (wt. %), with cerium constitutes increased to 50% of the total rare-earth content, was used. And Ce-free Nd{sub 30}Fe{sub bal}B{sub 1} (wt. %) was prepared by the same preparation process as comparison. The microstructure of the sintered magnets has been investigated by means of X-ray diffraction and transmission electron microscope. The results show that there are three kinds of RE-rich phases in the same magnet, i.e., fcc-(Ce,Nd)O{sub x} (a=0.547nm), hcp-(Ce,Nd){sub 2}O{sub 3} (a=0.386nm, c=0.604nm) and bcc-(Ce,Nd){sub 2}O{sub 3} (a=1.113nm). Ors of (140)(Ce,Nd){sub 2}Fe{sub 14}B// (1-21)bcc-(Ce,Nd){sub 2}O{sub 3}(∼3°), [001](Ce,Nd){sub 2}Fe{sub 14}B// [-214]bcc-(Ce,Nd){sub 2}O{sub 3}; (01-1)(Ce,Nd){sub 2}Fe{sub 14}B// (101)fcc- (Ce,Nd)O{sub x}(∼2°), [101](Ce,Nd){sub 2}Fe14B// [12-1]fcc-(Ce,Nd)O{sub x} were found through selected area electron diffraction (SAED) analysis. According to the analysis, it can be concluded that cerium has partly substituted for neodymium by occupying the corresponding atom sites in the Ce{sub 15}Nd{sub 15}Fe{sub bal}B{sub 1} magnet, without changing the crystal configuration.
Authors:
 [1] ;  [2] ;  [2] ; ; ; ;  [1] ;  [2] ;  [3]
  1. Functional Materials Research Institute, Central Iron and Steel Research Institute, Beijing 100081 (China)
  2. (China)
  3. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China)
Publication Date:
OSTI Identifier:
22299624
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Advances; Journal Volume: 4; Journal Issue: 10; Other Information: (c) 2014 Author(s); Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; BCC LATTICES; CERIUM; CHEMICAL COMPOSITION; CRYSTALS; DEUTERIDES; ELECTRON DIFFRACTION; FCC LATTICES; HCP LATTICES; MAGNETS; MICROSTRUCTURE; NEODYMIUM; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION