Phase equilibria in the quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} and physical properties of (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} single crystals
- Department of Inorganic and Physical Chemistry, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)
- Department of General Physics, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)
The quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} was investigated by differential thermal, X-ray phase, X-ray structure, microstructure analysis and microhardness measurements. Five quasi-binary phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were constructed. The character and temperature of the invariant processes were determined. The specific resistance of the single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} was measured, 7.5×10{sup 5} and 3.15×10{sup 5} Ω m, respectively, optical absorption spectra in the 600–1050 nm range were recorded at room temperature, and the band gap energy was estimated which is 1.95±0. 01 eV for both samples. - Graphical abstract: The article reports for the first time the investigated liquidus surface projection of the Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system and isothermal section at 820 K of the system. Five phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were built at the first time. The existence of the large region of the solid solutions based on AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} was investigated. The existence of two ternary phases was established in the Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system. Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown and some of optical properties of them were studied at first time. Display Omitted - Highlights: • Liquidus surface projection was built for Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system. • Solid solution ranges of AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} were investigated. • Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown. • Some optical properties of these single crystals were studied.
- OSTI ID:
- 22274200
- Journal Information:
- Journal of Solid State Chemistry, Vol. 210, Issue 1; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Phase equilibria in the quasiternary system Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} and optical properties of (Ga{sub 55}In{sub 45}){sub 2}S{sub 300}, (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} single crystals
The Sb-Sb/sub 2/Se/sub 3/-SbI/sub 3/ system