Modelling the graphite fracture mechanisms
- CEA Saclay, Gif-sur-Yvette, (France)
- IRSN/PSN-EXP/SES, Fontenay-aux-Roses, (France)
In order to define a design criterion for graphite components, it is important to identify the physical phenomena responsible for the graphite fracture, to include them in a more effective modelling. In a first step, a large panel of experiments have been realised in order to build up an important database; results of tensile tests, 3 and 4 point bending tests on smooth and notched specimens have been analysed and have demonstrated an important geometry related effects on the behavior up to fracture. Then, first simulations with an elastic or an elastoplastic bilinear constitutive law have not made it possible to simulate the experimental fracture stress variations with the specimen geometry, the fracture mechanisms of the graphite being at the microstructural scale. That is the reason why a specific F.E. model of the graphite structure has been developed in which every graphite grain has been meshed independently, the crack initiation along the basal plane of the particles as well as the crack propagation and coalescence have been modelled too. This specific model has been used to test two different approaches for fracture initiation: a critical stress criterion and two criteria of fracture mechanic type. They are all based on crystallographic considerations as a global critical stress criterion gave unsatisfactory results. The criteria of fracture mechanic type being extremely unstable and unable to represent the graphite global behaviour up to the final collapse, the critical stress criterion has been preferred to predict the results of the large range of available experiments, on both smooth and notched specimens. In so doing, the experimental observations have been correctly simulated: the geometry related effects on the experimental fracture stress dispersion, the specimen volume effects on the macroscopic fracture stress and the crack propagation at a constant stress intensity factor. In addition, the parameters of the criterion have been related to experimental observations: the local crack initiation stress of 8 MPa corresponds to the non-linearity apparition on the global behavior observed experimentally and the the maximal critical stress defined for the particle of 30 MPa is equivalent to the fracture stress of notched specimens. This innovative combination of crack modelling and a local crystallographic critical stress criterion made it possible to understand that cleavage initiation and propagation in the graphite microstructure was driven by a mean critical stress criterion. (authors)
- OSTI ID:
- 22273974
- Resource Relation:
- Conference: PVP2012: ASME 2012 Pressure Vessels and Piping Conference, Toronto, Ontario (Canada), 15-19 Jul 2012; Other Information: Country of input: France; This record replaces 45095207
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure Anisotropy Effects on Fracture and Fatigue Mechanisms in Shape Memory Alloy Martensites
The influences of hydride size and matrix strength on fracture initiation at hydrides in zirconium alloys