Title: Magnetic properties of Ni substituted Y-type barium ferrite

Abstract

Y-type barium hexaferrite is attractive material for various applications, such as high frequency antennas and RF devices, because of its interesting magnetic properties. Especially, Ni substituted Y- type hexaferrites have higher magnetic ordering temperature than other Y-type. We have investigated macroscopic and microscopic properties of Y-type barium hexaferrite. Ba{sub 2}Co{sub 2−x}Ni{sub x}Fe{sub 12}O{sub 22} (x = 0, 0.5, 1.0, 1.5, and 2.0) samples are prepared by solid-state reaction method and studied by X-ray diffraction (XRD), vibrating sample magnetometer, and Mössbauer spectroscopy, as well as a network analyzer for high frequency characteristics. The XRD pattern is analyzed by Rietveld refinement method and confirms the hexagonal structure with R-3m. The hysteresis curve shows ferrimagnetic behavior. Saturation magnetization (M{sub s}) decreases with Ni contents. Ni{sup 2+}, which preferentially occupies the octahedral site with up-spin sub-lattice, has smaller spin value S of 1 than Co{sup 2+} having S = 3/2. The zero-field-cooled (ZFC) measurement of Ba{sub 2}Co{sub 1.5}Ni{sub 0.5}Fe{sub 12}O{sub 22} shows that Curie and spin transition temperatures are found to be 718 K and 209 K, respectively. The Curie temperature T{sub C} is increased with Ni contents, while T{sub S} is decreased with Ni. The Mössbauer spectra were measured at various temperatures and fitted by using a least-squares methodmore » with six sextet of six Lorentzian lines for Fe sites, corresponding to the 3b{sub VI}, 6c{sub IV}*, 6c{sub VI}, 18h{sub VI}, 6c{sub IV}, and 3a{sub IV} sites at below T{sub C}. From Mössbauer measurements, we confirmed the spin state of Fe ion to be Fe{sup 3+} and obtained the isomer shift (δ), magnetic hyperfine field (H{sub hf}), and the occupancy ratio of Fe ions at six sub-lattices. The complex permeability and permittivity are measured between 100 MHz and 4 GHz, suggesting that Y-type barium hexaferrite is promising for antenna applications in UHF band.« less

Authors:
Publication Date:
OSTI Identifier:
22273871
Resource Type:
Journal Article
Journal Name:
Journal of Applied Physics
Additional Journal Information:
Journal Volume: 115; Journal Issue: 17; Conference: 55. annual conference on magnetism and magnetic materials, Atlanta, GA (United States), 14-18 Nov 2010; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); Journal ID: ISSN 0021-8979
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ABSORPTION SPECTROSCOPY; BARIUM COMPOUNDS; COBALT IONS; CURIE POINT; FERRIMAGNETISM; FERRITES; HYSTERESIS; IRON IONS; ISOMER SHIFT; LEAST SQUARE FIT; MAGNETIC PROPERTIES; MAGNETIZATION; MOESSBAUER EFFECT; NICKEL IONS; PERMEABILITY; PERMITTIVITY; SPIN; VIBRATING SAMPLE MAGNETOMETERS; X-RAY DIFFRACTION

Citation Formats

Won, Mi Hee, and Kim, Chul Sung, E-mail: cskim@kookmin.ac.kr. Magnetic properties of Ni substituted Y-type barium ferrite. United States: N. p., 2014. Web. doi:10.1063/1.4860939.
Won, Mi Hee, & Kim, Chul Sung, E-mail: cskim@kookmin.ac.kr. Magnetic properties of Ni substituted Y-type barium ferrite. United States. https://doi.org/10.1063/1.4860939
Won, Mi Hee, and Kim, Chul Sung, E-mail: cskim@kookmin.ac.kr. 2014. "Magnetic properties of Ni substituted Y-type barium ferrite". United States. https://doi.org/10.1063/1.4860939.
@article{osti_22273871,
title = {Magnetic properties of Ni substituted Y-type barium ferrite},
author = {Won, Mi Hee and Kim, Chul Sung, E-mail: cskim@kookmin.ac.kr},
abstractNote = {Y-type barium hexaferrite is attractive material for various applications, such as high frequency antennas and RF devices, because of its interesting magnetic properties. Especially, Ni substituted Y- type hexaferrites have higher magnetic ordering temperature than other Y-type. We have investigated macroscopic and microscopic properties of Y-type barium hexaferrite. Ba{sub 2}Co{sub 2−x}Ni{sub x}Fe{sub 12}O{sub 22} (x = 0, 0.5, 1.0, 1.5, and 2.0) samples are prepared by solid-state reaction method and studied by X-ray diffraction (XRD), vibrating sample magnetometer, and Mössbauer spectroscopy, as well as a network analyzer for high frequency characteristics. The XRD pattern is analyzed by Rietveld refinement method and confirms the hexagonal structure with R-3m. The hysteresis curve shows ferrimagnetic behavior. Saturation magnetization (M{sub s}) decreases with Ni contents. Ni{sup 2+}, which preferentially occupies the octahedral site with up-spin sub-lattice, has smaller spin value S of 1 than Co{sup 2+} having S = 3/2. The zero-field-cooled (ZFC) measurement of Ba{sub 2}Co{sub 1.5}Ni{sub 0.5}Fe{sub 12}O{sub 22} shows that Curie and spin transition temperatures are found to be 718 K and 209 K, respectively. The Curie temperature T{sub C} is increased with Ni contents, while T{sub S} is decreased with Ni. The Mössbauer spectra were measured at various temperatures and fitted by using a least-squares method with six sextet of six Lorentzian lines for Fe sites, corresponding to the 3b{sub VI}, 6c{sub IV}*, 6c{sub VI}, 18h{sub VI}, 6c{sub IV}, and 3a{sub IV} sites at below T{sub C}. From Mössbauer measurements, we confirmed the spin state of Fe ion to be Fe{sup 3+} and obtained the isomer shift (δ), magnetic hyperfine field (H{sub hf}), and the occupancy ratio of Fe ions at six sub-lattices. The complex permeability and permittivity are measured between 100 MHz and 4 GHz, suggesting that Y-type barium hexaferrite is promising for antenna applications in UHF band.},
doi = {10.1063/1.4860939},
url = {https://www.osti.gov/biblio/22273871}, journal = {Journal of Applied Physics},
issn = {0021-8979},
number = 17,
volume = 115,
place = {United States},
year = {Wed May 07 00:00:00 EDT 2014},
month = {Wed May 07 00:00:00 EDT 2014}
}