Growth and characterization of ZnSe nanoparticles
Journal Article
·
· AIP Conference Proceedings
ZnSe nanoparticles were prepared using a chemical bath deposition technique. X-ray diffraction study shows that the ZnSe crystallizes in the cubic phase. The crystallite size of the ZnSe samples calculated using the Scherrer’s formula was found to be slightly smaller than the Bohr exciton radius of bulk ZnSe. SEM studies show the growth of a mixture of nanorods and spherical nanoparticles. EDAX analysis confirms that the synthesized ZnSe nanoparticles are of good stiochiometry. Optical studies show the blue shift in the absorption edge for ZnSe nanoparticles caused by quantum confinement.
- OSTI ID:
- 22269490
- Journal Information:
- AIP Conference Proceedings, Vol. 1591, Issue 1; Conference: 58. DAE solid state physics symposium 2013, Patiala, Punjab (India), 17-21 Dec 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis, structural and optical properties of Sm{sup 3+} and Nd{sup 3+} doped cadmium sulfide nanocrystals
Investigations on the electronic properties and effect of chitosan capping on the structural and optical properties of zinc aluminate quantum dots
Synthesis, characterization, photocatalytic activity and ethanol-sensing properties of In{sub 2}O{sub 3} and Eu{sup 3+}:In{sub 2}O{sub 3} nanoparticles
Journal Article
·
Tue Apr 01 00:00:00 EDT 2014
· Materials Research Bulletin
·
OSTI ID:22269490
+2 more
Investigations on the electronic properties and effect of chitosan capping on the structural and optical properties of zinc aluminate quantum dots
Journal Article
·
Fri Dec 10 00:00:00 EST 2021
· Applied Surface Science
·
OSTI ID:22269490
+3 more
Synthesis, characterization, photocatalytic activity and ethanol-sensing properties of In{sub 2}O{sub 3} and Eu{sup 3+}:In{sub 2}O{sub 3} nanoparticles
Journal Article
·
Fri May 15 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:22269490
+1 more