Ionic conductivity of Bi{sub 2}Ni{sub x}V{sub 1−x}O{sub 5.5−3x/2} (0.1 ≤ x ≤ 0.2) oxides prepared by a low temperature sol-gel route
- Inorganic and Physical Chemistry Division, Faculty of Mathematics and Natural Sciences, Institut Teknologi Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia)
- Materials Research Institute, School of Biological and Chemical Sciences, Queen Mary University of London, Mile End Road, London E1 4NS (United Kingdom)
Solid oxides fuel cells (SOFCs) is one technology that could contribute toward future sustainable energy. One of the most important components of an SOFC is the electrolyte, which must have high ionic conductivity. Cation substitution of vanadium in Bi{sub 4}V{sub 2}O{sub 11} yields a family of fast oxide ion conducting solids known collectively as the BIMEVOXes (bismuth metal vanadium oxide), which have the potential to be applied as electrolytes in SOFCs. The purpose of this work is to study the effect of Ni concentration, when used as a dopant, on the ionic conductivity of Bi{sub 2}Ni{sub x}V{sub 1−x}O{sub 5.5−3x/2} (BINIVOX) oxides (0.1 ≤ x ≤ 0.2) when prepared by a sol gel method. The gels were calcined at 600 °C for 24 h to produce pure BINIVOX. These oxides were found to exhibit the γ-phase structure with tetragonal symmetry in space group I4/mmm. Ionic conductivity of BINIVOX at 300 °C were 6.9 × 10{sup −3} S cm{sup −1}, 1.2 × 10{sup −3} S cm{sup −1}, and 8.2 × 10{sup −4} S cm{sup −1}, for x = 0.1; 0.15; and 0.2; respectively; and at 600 °C were 1.1 × 10{sup −1} S cm{sup −1}, 5.3 × 10{sup −2} S cm{sup −1}, and 2.8 ×10{sup −2} S cm{sup −1}, for x = 0.1; 0.15; and 0.2; respectively.
- OSTI ID:
- 22265960
- Journal Information:
- AIP Conference Proceedings, Vol. 1589, Issue 1; Conference: ICMNS 2012: 4. international conference on mathematics and natural sciences: Science for health, food and sustainable energy, Bandung (Indonesia), 8-9 Nov 2012; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis, Processing and Properties of Calcium- and Nickel-Doped Yttrium Chromates(III) Y{sub 0.8}Ca{sub 0.2}Cr{sub 1−x}Ni{sub x}O{sub 3} (x = 0-0.3) and Studies on Their Potential Application as Coatings for SOFC Interconnects
Synthesis and electrical properties of scheelite Ca{sub 1-x}Sm{sub x}MoO{sub 4+{delta}} solid electrolyte ceramics