Precipitation method for barium metaborate (BaB{sub 2}O{sub 4}) synthesis from borax solution
- Yildiz Technical University, Chem. Eng. Dept., Davutpasa Campus, 34210, Istanbul (Turkey)
In this study, barium metaborate (BaB{sub 2}O{sub 4}, BMB) synthesis from the borax solution was carried out. BMB currently is used in production of ceramic glazes, luminophors, oxide cathodes as well as additives to pigments for aqueous emulsion paints and also β−BaB{sub 2}O{sub 4} single crystals are the best candidate for fabrication of solid-state UV lasers operating at a wavelength of 200 nm due to excellent nonlinear optical properties. In the present study, synthesis was carried out from the borax solution (Na{sub 2}B{sub 4}O{sub 7⋅}10H{sub 2}O, BDH) and barium chloride (BaCI{sub 2⋅}2H{sub 2}O, Ba) in the glass-batch reactor with stirring. The effect of, times (5-15 min), molar ratio [stoich.ration (1.0:2.0), 1.25:2.0, 1.5:2.0, 2.5:2:0, 3.0:2.0, 3.5:2.0,4.0:2.0, 5.0:2.0] and also crystallization time (2-6 hour) on the BMB yield (%) was investigated at 80 °C reaction temperature. It is found that, BMB precipitation synthesis with 90 % yield can be performed from 0.50 molar ration (BDH:Ba), under 80 °C, 15 minute, and 6 hours crystallization time. The structural properties of BMB powders were characterized by using XRD, FT-IR and DTA-TG instrumental analysis technique.
- OSTI ID:
- 22261699
- Journal Information:
- AIP Conference Proceedings, Vol. 1569, Issue 1; Conference: 3. international advances in applied physics and materials science congress, Antalya (Turkey), 24-28 Apr 2013; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
A new BaB{sub 2}Si{sub 2}O{sub 8}:Eu{sup 2+}/Eu{sup 3+}, Tb{sup 3+} phosphor - Synthesis and photoluminescence properties
Structural studies in the BaO-B{sub 2}O{sub 3}-TiO{sub 2} system by XAS and {sup 11}B-NMR