Early age hydration of calcium sulfoaluminate (synthetic ye'elimite, C{sub 4}A{sub 3}S{sup ¯}) in the presence of gypsum and varying amounts of calcium hydroxide
- Department of Civil and Environmental Engineering, University of California, Berkeley, CA (United States)
- Department of Civil Engineering, Federal University of Rio Grande do Sul, Porto Alegre, RS (Brazil)
- Lafarge Centre de Recherche, St. Quentin Fallavier, Isere (France)
Suspensions of synthetic ye'elimite (C{sub 4}A{sub 3}S{sup ¯}) in a saturated gypsum (CS{sup ¯}H{sub 2}) and calcium hydroxide (CH) solution were examined in-situ in a wet cell by soft X-ray transmission microscopy and ex-situ by scanning electron microscopy. The most voluminous hydration product observed was ettringite. Ettringite commonly displayed acicular, filiform, reticulated, and stellate crystal habits. Additionally, pastes with C{sub 4}A{sub 3}S{sup ¯}, 15% CS{sup ¯}H{sub 2}, and varying amounts of CH were prepared and examined with X-ray diffraction (XRD) and isothermal calorimetry. The XRD experiments showed that increasing CH content caused more solid solution (SO{sub 4}{sup 2−}/OH{sup −}) AFm phases to form at early ages (< 1 d) and more monosulfate to form at later ages (> 1 d). Calorimetry indicated that the increased production of solid solution AFm was accompanied with an increase in the initial (< 30 min) rate of heat evolution, and increasing CH generally reduced the time till the second maximum rate of heat evolution due to the formation of ettringite and monosulfate.
- OSTI ID:
- 22220799
- Journal Information:
- Cement and Concrete Research, Vol. 48; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydration of calcium sulfoaluminate cements - Experimental findings and thermodynamic modelling
Hydration mechanisms of two polymorphs of synthetic ye'elimite