Ion irradiation of Fe-Fe oxide core-shell nanocluster films: Effect of interface on stability of magnetic properties
- Pacific Northwest National Laboratory, 902 Battelle Blvd., PO Box 999, Richland, Washington 99352 (United States)
- Department of Physics, University of Idaho, Moscow, Idaho 83844 (United States)
- Department of Physics, University of California, Davis, California 95616 (United States)
A cluster deposition method was used to produce films of loosely aggregated nanoclusters (NCs) of Fe core-Fe{sub 3}O{sub 4} shell or fully oxidized Fe{sub 3}O{sub 4}. Films of these NC on Si(100) or MgO(100)/Fe{sub 3}O{sub 4}(100) were irradiated to 10{sup 16} Si{sup 2+}/cm{sup 2} near room temperature using an ion accelerator. Ion irradiation creates structural change in the NC film with corresponding chemical and magnetic changes which depend on the initial oxidation state of the cluster. Films were characterized using magnetometry (hysteresis, first order reversal curves), microscopy (transmission electron, helium ion), and x-ray diffraction. In all cases, the particle sizes increased due to ion irradiation, and when a core of Fe is present, irradiation reduces the oxide shells to lower valent Fe species. These results show that ion irradiated behavior of the NC films depends strongly on the initial nanostructure and chemistry, but in general saturation magnetization decreases slightly.
- OSTI ID:
- 22218100
- Journal Information:
- Journal of Applied Physics, Vol. 114, Issue 8; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and magnetic properties of irradiated Fe-Fe oxide core-shell nanoclusters
Oxide shell reduction and magnetic property changes in core-shell Fe nanoclusters under ion irradiation