One component metal sintering additive for {beta}-SiC based on thermodynamic calculation and experimental observations
- School of Materials Science and Engineering, Yeungnam University, Gyeongsan 712-749 (Korea, Republic of)
Graphical abstract: . Standard Gibbs formation free energies vs. temperature for various metal carbides. The heavy line represents the standard Gibbs free energy for {beta}-SiC. The hatched area denotes the typical liquid phase hot pressing temperature of {beta}-SiC (1973-2123 K). Highlights: {yields} Various metal elements were examined as a sintering additive for {beta}-SiC. {yields} Al and Mg enhanced the density significantly without decomposing {beta}-SiC, as predicted by thermodynamic simulation. {yields} Cr, Fe, Ta, Ti, V and W additives formed metal carbide and/or silicide compounds by decomposing {beta}-SiC. {yields} This approach would be useful for selecting effective sintering additive for high temperature ceramics. -- Abstract: Various types of metals were examined as sintering additives for {beta}-SiC by considering the standard Gibbs formation free energy and vapor pressure under hot pressing conditions (1973-2123 K), particularly for applications in nuclear reactors. Metallic elements having the low long-term activation under neutron irradiation condition, such as Cr, Fe, Ta, Ti, V and W, as well as widely used elements, Al, Mg and B, were considered. The conclusions drawn from thermodynamic considerations were compared with the experimental observations. Al and Mg were found to be effective sintering additives, whereas the others were not due to the formation of metal carbides or silicides from the decomposition of SiC under hot pressing conditions.
- OSTI ID:
- 22212206
- Journal Information:
- Materials Research Bulletin, Vol. 46, Issue 8; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
DEVELOPMENT AND EVALUATION OF HIGH-TEMPERATURE TUNGSTEN ALLOYS. Period covered: May 1, 1957 to September 30, 1958
PROGRESS RELATING TO CIVILIAN APPLICATIONS DURING APRIL 1959