Preparation of nanocrystalline MgO by surfactant assisted precipitation method
- Catalyst and Advanced Materials Research Laboratory, Chemical Engineering Department, Faculty of Engineering, University of Kashan, Kashan (Iran, Islamic Republic of)
Highlights: {yields} Nanocrystalline magnesium oxide with high surface area. {yields} MgO prepared with surfactant showed different morphologies compared with the sample prepared without surfactant. {yields} MgO prepared with surfactant showed a plate-like shape. {yields} Refluxing temperature and time and the surfactant to metal molar ratio affect the textural properties of MgO. -- Abstract: Nanocrystalline magnesium oxide with high surface area was prepared by a simple precipitation method using pluronic P123 triblock copolymer (Poly (ethylene glycol)-block, Poly (propylene glycol)-block, Poly (ethylene glycol)) as surfactant and under refluxing conditions. The prepared samples were characterized by X-ray diffraction (XRD), N{sub 2} adsorption (BET) and scanning and transmission electron microscopies (SEM and TEM). The obtained results revealed that the refluxing time and temperature and the molar ratio of surfactant to metal affect the structural properties of MgO, because of the changes in the rate and extent of P123 adsorption on the prepared samples. The results showed that the addition of surfactant is effective to prepare magnesium oxide with high surface area and affects the morphology of the prepared samples. With increasing the P123/MgO molar ratio to 0.05 the pore size distribution was shifted to larger size. The sample prepared with addition of surfactant showed a plate-like shape which was completely different with the morphology of the sample prepared without surfactant. The formation of nanoplate-like MgO was related to higher surface density of Mg ions on the (0 0 1) plane than that on the other planes of the Mg(OH){sub 2} crystal. The (0 0 1) plane would be blocked preferentially by the adsorbed P123 molecules during the growing process of Mg(OH){sub 2} nanoentities and the growth on the (0 0 1) plane would be markedly restricted, and the consequence is the generation of nanoplate-like MgO. In addition, increase in refluxing temperature and time increased the specific surface area of the prepared MgO samples.
- OSTI ID:
- 22210080
- Journal Information:
- Materials Research Bulletin, Vol. 46, Issue 10; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Shape-controlled synthesis of gold icosahedra and nanoplates using Pluronic P123 block copolymer and sodium chloride
Transition metal-chelating surfactant micelle templates for facile synthesis of mesoporous silica nanoparticles
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
36 MATERIALS SCIENCE
77 NANOSCIENCE AND NANOTECHNOLOGY
ADSORPTION
CRYSTALS
MAGNESIUM OXIDES
NANOSTRUCTURES
POLYETHYLENE GLYCOLS
PRECIPITATION
SCANNING ELECTRON MICROSCOPY
SPECIFIC SURFACE AREA
SURFACE AREA
SURFACES
SURFACTANTS
SYNTHESIS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION