Re-entrant relaxor behavior of Ba{sub 5}RTi{sub 3}Nb{sub 7}O{sub 30} (R = La, Nd, Sm) tungsten bronze ceramics
- Department of Materials Science and Engineering, Zhejiang University, 38 Zheda Road, Hangzhou 310027 (China)
Ba{sub 5}RTi{sub 3}Nb{sub 7}O{sub 30} (R = La, Nd, Sm) tungsten bronze ceramics were prepared, and the dielectric and ferroelectric properties were investigated over a broad temperature range. The relaxor nature was determined for all compositions in their permittivity curves, and a second anomaly of the dielectric loss (tan {delta}) was observed around 250 K in Ba{sub 5}NdTi{sub 3}Nb{sub 7}O{sub 30} and around 275 K in Ba{sub 5}SmTi{sub 3}Nb{sub 7}O{sub 30}. Both the maximum and remanent polarization tended to decrease and vanish at low temperatures in the ferroelectric phase for all compositions, which was referred to as the low temperature re-entrant relaxor behavior. The remanent polarization increased with decreasing temperature first and then reached the maximum value at the re-entrant temperature (T{sub r}). For Ba{sub 5}RTi{sub 3}Nb{sub 7}O{sub 30} (R = La, Nd, Sm), T{sub r} decreased with the radius of R{sup 3+} cations and the applied field amplitude.
- OSTI ID:
- 22162800
- Journal Information:
- Applied Physics Letters, Vol. 102, Issue 11; Other Information: (c) 2013 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and dielectric properties of Ba{sub 5}NdCu{sub 1.5}Nb{sub 8.5}O{sub 30−δ} tungsten bronze ceramics
Enhanced characteristics of Ba{sub 5}SmTi{sub 3}Nb{sub 7}O{sub 30} ferroelectric nanocrystalline ceramic prepared by mechanical activation process: A comparative study