Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er)
- Department of Materials Science and Technology, Nagaoka University of Technology, 1603-1 Kamitomioka-cho, Nagaoka 940-2188 (Japan)
Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze (TTB) structure are synthesized using a conventional glass crystallization technique in 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} (mol%) (RE=Sm, Eu, Gd, Dy, and Er) glasses. One sharp crystallization peak is observed at {approx}670 Degree-Sign C in both powdered and bulk glasses, and the formation of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with unit cell parameters of a{approx}1.24 nm and c{approx}0.39 nm was confirmed. It is found from high resolution transmission electron microscope observations that the morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Their average particle size is in the range of 15-60 nm and decreases with decreasing ionic radius of RE{sup 3+} being present in the precursor glasses. The optical transparent crystallized glass (bulk) shows the total photoluminescence (PL) quantum yield of 53% in the visible region of Eu{sup 3+} ions, suggesting a high potential of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals as PL materials. - Graphical abstract: This figure shows a TEM photograph for the heat-treated (667 Degree-Sign C, 3 h) sample of 2.3Dy{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3}. An ellipsoidal-shaped Ba{sub 1-x}Dy{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystal with diameters of 17 and 28 nm is observed. The ellipsoidal morphology is a common feature in Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals synthesized by the crystallization of 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} glasses. Highlights: Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze structure are synthesized. Black-Right-Pointing-Pointer A glass crystallization technique was applied. Black-Right-Pointing-Pointer The morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Black-Right-Pointing-Pointer The average particle size with 15-60 nm decreases with decreasing ionic radius of RE{sup 3+}. Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals have a high potential as photoluminescence materials.
- OSTI ID:
- 22149959
- Journal Information:
- Journal of Solid State Chemistry, Vol. 196; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and physical properties of Re substituted B-site ordered and disordered SrCo{sub 1-x}Re{sub x}O{sub 3-{delta}} (x=0.1, 0.25, 0.5)
Thermal expansion of lanthanum silicate oxyapatite (La{sub 9.33+2x}(SiO{sub 4}){sub 6}O{sub 2+3x}), lanthanum oxyorthosilicate (La{sub 2}SiO{sub 5}) and lanthanum sorosilicate (La{sub 2}Si{sub 2}O{sub 7})
Related Subjects
77 NANOSCIENCE AND NANOTECHNOLOGY
37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
BARIUM OXIDES
BORON OXIDES
CRYSTALLIZATION
EUROPIUM IONS
GLASS
MORPHOLOGY
NANOSTRUCTURES
NIOBATES
NIOBIUM OXIDES
PARTICLE SIZE
PHOTOLUMINESCENCE
TRANSMISSION ELECTRON MICROSCOPY
TUNGSTEN BRONZE