Pump-beam-induced optical damage depended on repetition frequency and pulse width in 4-dimethylamino-N Prime -methyl-4 Prime -stilbazolium tosylate crystal
- Tera-photonics Laboratory, RIKEN, 519-1399, Aramaki-Aoba, Aoba-ku, Sendai 980-0845 (Japan)
We investigated the dependence of optical damage to an organic nonlinear optical crystal of 4-dimethylamino-N Prime -methyl-4 Prime -stilbazolium tosylate (DAST) on the repetition frequency and pulse width of the pump beam used to cause the thermal damage. For a pump beam with a pulse width of 15 ns at a wavelength of 1064 nm, the highest damage threshold of 8.0 J/cm{sup 2} was measured for repetition frequencies in the range from 10 to 40 Hz. On the other hand, DAST crystals were easily damaged under the repetition rates from 50 to 100 Hz. For 600-ps pulses, a higher damage threshold that was a factor of 11 to 28 times higher in terms of peak intensity was obtained compared with that of 15-ns pulses. In both the cases of 15-ns pulse duration and 600-ps duration, we demonstrated that the thermal effects in DAST crystals dominated the optical damage, which depended on thermal accumulation and dissipation.
- OSTI ID:
- 22122792
- Journal Information:
- Applied Physics Letters, Vol. 103, Issue 2; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electro-Optic Sampling System with a Single-Crystal 4-N, N-Dimethylamino-4'-N'-Methyl-4-Stilbazolium Tosylate Sensor
Growth and characterization of 4-dimethylamino-N-methyl 4-stilbazolium tosylate (DAST) single crystals grown by nucleation reduction method