Indium and impurity incorporation in InGaN films on polar, nonpolar, and semipolar GaN orientations grown by ammonia molecular beam epitaxy
- Materials Department, University of California Santa Barbara, Santa Barbara, California 93106 (United States)
The effects of NH{sub 3} flow, group III flux, and substrate growth temperature on indium incorporation and surface morphology have been investigated for bulk InGaN films grown by ammonia molecular beam epitaxy. The incorporation of unintentional impurity elements (H, C, O) in InGaN films was studied as a function of growth temperature for growth on polar (0001) GaN on sapphire templates, nonpolar (1010) bulk GaN, and semipolar (1122), (2021) bulk GaN substrates. Enhanced indium incorporation was observed on both (1010) and (2021) surfaces relative to c-plane, while reduced indium incorporation was observed on (1122) for co-loaded conditions. Indium incorporation was observed to increase with decreasing growth temperature for all planes, while being relatively unaffected by the group III flux rates for a 1:1 Ga:In ratio. Indium incorporation was found to increase at the expense of a decreased growth rate for higher ammonia flows; however, smooth surface morphology was consistently observed for growth on semipolar orientations. Increased concentrations of oxygen and hydrogen were observed on semipolar and nonpolar orientations with a clear trend of increased hydrogen incorporation with indium content.
- OSTI ID:
- 22098906
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Vol. 30, Issue 4; Other Information: (c) 2012 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 0734-2101
- Country of Publication:
- United States
- Language:
- English
Similar Records
Strain relaxation of thick (11–22) semipolar InGaN layer for long wavelength nitride-based device
Semipolar and nonpolar GaN epi-films grown on m-sapphire by plasma assisted molecular beam epitaxy