Lattice variations of Ti-6Al-4V alloy with hydrogen content
Effect of hydrogen content on the lattice parameter of Ti-6Al-4V alloy has been investigated by X-ray diffraction. The experimental results show that the solution of hydrogen in the Ti-6Al-4V alloy affects significantly on the lattice parameters of {alpha}, {beta} and {delta} phases, especially the {beta} phase. Furthermore, the critical hydrogen content of {delta} hydride formation for Ti-6Al-4V alloy is 0.385 wt.%. When the hydrogen content is lower than the critical hydrogen content, the {delta} hydride cannot precipitate and the lattice parameter ({alpha}) of {beta} phase linearly increases with the increasing of hydrogen content. When the hydrogen content is higher than the critical hydrogen content, the {delta} hydride precipitates and the lattice parameter ({alpha}) of {beta} phase varies inconspicuously with hydrogen content. In addition, the effects of lattice variations and {delta} hydride formation on microstructure are discussed. The {alpha}/{beta} interfaces of lamellar transformed {beta} phase become fuzzy with the increasing of hydrogen content because of the lattice expansion of {beta} phase. Compared with that of the Ti-6Al-4V alloy at low hydrogen content ({<=} 0.385 wt.%), the contrasts of primary {alpha} phase and transformed {beta} phase of Ti-6Al-4V alloy at high hydrogen content ({>=} 0.385 wt.%) were completely reversed due to the formation of {delta} hydride. - Research Highlights: {yields} A novel method for determining {delta} hydride in Ti-6Al-4V alloy is presented. {yields} The critical hydrogen content of {delta} hydride formation is 0.385 wt.%. {yields} The lattice parameter of {beta} phase can be expressed as follows: a=0.323(1+9.9x10{sup -2}C{sub H}) . {yields} Precipitation of {delta} hydride has a significant influence on the microstructure. {yields} The {alpha}/{beta} interfaces of transformed {beta} phase became fuzzy in the hydrogenated alloy.
- OSTI ID:
- 22066371
- Journal Information:
- Materials Characterization, Vol. 62, Issue 7; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE TRANSFORMATION OF $alpha$ + $beta$ TITANIUM ALLOYS WITH ALUMINUM
Evidence of FCC titanium hydride formation in. beta. titanium alloy: An X-ray diffraction study