Phase transformations in the Zn-Al eutectoid alloy after quenching from the high temperature triclinic beta phase
Journal Article
·
· Materials Characterization
- Instituto Nacional de Investigaciones Nucleares, Dpto. de Aceleradores, Carretera Mexico-Toluca S/N, La Marquesa, Ocoyoacac, Mexico, C.P. 52750, ESIME, Unidad Culhuacan, Dpto. Ing. Mecanica, IPN (Mexico)
- Instituto de Metalurgia, Universidad Autonoma de San Luis Potosi, SLP 78210 (Mexico)
- Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Apdo. Postal 70-360, Mexico D.F. 04510 (Mexico)
Ribbons of the Zn-Al eutectoid alloy obtained by melt-spinning, were heat treated at 350 deg. C during 30 min in a free atmosphere furnace, and then quenched in liquid nitrogen. The temperature correspond to {beta} phase zone, which has a triclinic crystalline structure [1, 2]. Some evidence, obtained by X-ray diffraction, show that the structures present in the just quenched material are both close-packed hexagonal ({eta}-phase) and rhombohedral (R-phase). X-ray diffractograms taken in the same ribbons after annealed 500 h at room temperature, show that the R phase its transform to {alpha} and {eta} phases.
- OSTI ID:
- 22066248
- Journal Information:
- Materials Characterization, Vol. 61, Issue 11; Other Information: Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
The triclinic high temperature modification of the {alpha} phase of the Zn-Al system
On the decomposition of {beta} phase in some rapidly quenched titanium-eutectoid alloys
Phase transformation of Zn-4Al-3Cu alloy during heat treatment
Journal Article
·
Wed Dec 01 00:00:00 EST 1999
· Materials Research Bulletin
·
OSTI ID:22066248
On the decomposition of {beta} phase in some rapidly quenched titanium-eutectoid alloys
Journal Article
·
Thu Jun 01 00:00:00 EDT 1995
· Metallurgical Transactions, A
·
OSTI ID:22066248
Phase transformation of Zn-4Al-3Cu alloy during heat treatment
Journal Article
·
Thu Apr 01 00:00:00 EST 1999
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:22066248