Characterization of the interaction layer in diffusion couples U-7 wt.%Mo/Al 6061 alloy at 550 deg. C and 340 deg. C
- Departamento Materiales, GAEN-GIDAT-CNEA, Av. Gral. Paz 1499, B1650KNA, San Martin (Argentina)
Solid state reaction between U-7 wt.%Mo and Al 6061 alloys at 550 deg. C and 340 deg. C was characterized in chemical diffusion couples made by Friction Stir Welding. Results were obtained from optical and scanning electron microscopy, electron probe microanalysis and X-ray diffraction. At 550 deg. C the interaction layer in {gamma}U(Mo)/Al 6061 is formed by U(Al,Si){sub 3} phase but when {gamma}U(Mo) cellular decomposition occurs, UAl{sub 3} and Al{sub 43}Mo{sub 4}U{sub 6} also appear in the interaction layer. At 340 deg. C the use of X-ray diffraction with synchrotron radiation made it possible to analyze the interaction layer. It was found that it is only formed by U{sub 3}Si{sub 5} phase with its cell volume enlarged respect to the original one.
- OSTI ID:
- 22066116
- Journal Information:
- Materials Characterization, Vol. 60, Issue 8; Other Information: Copyright (c) 2009 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Identification of phases in the interaction layer between U-Mo-Zr/Al and U-Mo-Zr/Al-Si
ISOTHERMAL TRANSFORMATION OF U-14 AND U-16 WT % Mo ALLOYS AT 550 C. Interim Report