A new BaB{sub 2}Si{sub 2}O{sub 8}:Eu{sup 2+}/Eu{sup 3+}, Tb{sup 3+} phosphor - Synthesis and photoluminescence properties
- Department of Chemistry, Indian Institute of Technology Madras, Chennai 600036 (India)
- Laboratoire de Cristallographie et Sciences des Materiaux, ENSICAEN, Universite de Caen, CNRS, 6 Bd Marechal Juin, F-14050 Caen (France)
In the present work, we have synthesized maleevite mineral phase BaB{sub 2}Si{sub 2}O{sub 8} for the first time, which is isostructural with the pekovite mineral SrB{sub 2}Si{sub 2}O{sub 8}. In these europium doped host lattices, we observed the partial reduction of Eu{sup 3+} to Eu{sup 2+} at high temperature during the synthesis in air. Tb{sup 3+} co-doping in MB{sub 2}Si{sub 2}O{sub 8}:0.01(Eu{sup 3+}/Eu{sup 2+}) [M=Sr, Ba] improves the emission properties towards white light. The emission color varies from bluish white to greenish white under UV lamp excitation when the host cation changes from Sr to Ba. - Graphical abstract: The figure shows structure refinement of both MB{sub 2}Si{sub 2}O{sub 8} [M=Sr, Ba]. The structure refinement of newly synthesized phase BaB{sub 2}Si{sub 2}O{sub 8} was carried out by taking SrB{sub 2}Si{sub 2}O{sub 8} as starting structure model. Inset in the figure shows the structure projection of BaB{sub 2}Si{sub 2}O{sub 8}. The Sr{sup 2+}/Ba{sup 2+} are embedded in polyanionic network formed by corner sharing BO{sub 4}{sup 5-} and SiO{sub 4}{sup 4-} tetrahedral that intern form interconnected layers of 4 and 8 membered rings perpendicular to b-axis.
- OSTI ID:
- 21421500
- Journal Information:
- Journal of Solid State Chemistry, Vol. 183, Issue 10; Other Information: DOI: 10.1016/j.jssc.2010.07.008; PII: S0022-4596(10)00290-2; Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
The effects of re-firing process under oxidizing atmosphere and temperatures on the properties of strontium aluminate phosphors
The effect of replacement of Sr by Ca on the structural and luminescence properties of the red-emitting Sr{sub 2}Si{sub 5}N{sub 8}:Eu{sup 2+} LED conversion phosphor
Related Subjects
BARIUM COMPOUNDS
BARIUM IONS
BORON SILICATES
DOPED MATERIALS
EUROPIUM IONS
PHOTOLUMINESCENCE
STRONTIUM IONS
SYNTHESIS
TERBIUM IONS
ALKALINE EARTH METAL COMPOUNDS
BORON COMPOUNDS
CHARGED PARTICLES
EMISSION
IONS
LUMINESCENCE
MATERIALS
OXYGEN COMPOUNDS
PHOTON EMISSION
SILICATES
SILICON COMPOUNDS