Development of modified MDA (M-MDA), PWR fuel cladding tube for high duty operation in future
- Mitsubishi Heavy Industries, LTD., 1-1-1, Wadasaki-cho, Hyogo-ku, KOBE 652-8585 (Japan)
- Nuclear Development Corporation, 622-12, Funaishikawa, Toka-mura, Naka-gun, Ibaraki 319-1111 (Japan)
- The Kansai Electric Power Co., INC., 8 Yokota, 13 Goichi, Mihama-cho, Mikata-gun, FUKUI-ken, 919-1141 (Japan)
A new cladding material of M-MDA has been developed in order to prepare for a strong growing demand for advanced fuel which can maintain its integrity even under high duties due to more efficient operation such as higher burnup, higher LHR, and longer operation cycle which will contribute the suppression of environmental burdens like CO{sub 2} emission. The main aim of M-MDA is to have excellent corrosion resistance while the other properties are inherited from MDA, which has been adopted to the step 2 fuel, instead of Zry-4, of Japanese PWR plant whose upper limit of assembly discharged burnup is 55 MWd/kgU. And we could confirm that the main aim of M-MDA was achieved by means of out-of-pile tests. In order to confirm improvement of corrosion resistance of M-MDA in the actual operation, irradiation test of M-MDA in the commercial reactor of Vandellos II is ongoing. The latest results of on-site examination after every end of cycle showed that oxide thickness of M-MDA-SR was much smaller than that of MDA at rod discharged burnup of approximately 60 MWd/kgU. The final irradiation cycle was completed on April 2007 and then we will obtain corrosion data of M-MDA over 70 MWd/kgU. M-MDA is a candidate alloy for advanced fuel under higher duty usage. (authors)
- Research Organization:
- American Nuclear Society, 555 North Kensington Avenue, La Grange Park, IL 60526 (United States)
- OSTI ID:
- 21229300
- Resource Relation:
- Conference: 2007 LWR Fuel Performance Meeting / TopFuel 2007, San Francisco, CA (United States), 30 Sep - 3 Oct 2007; Other Information: Country of input: France; 6 refs; Related Information: In: Proceedings of the 2007 LWR Fuel Performance Meeting / TopFuel 2007 'Zero by 2010', 683 pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Behavior of high-burnup advanced LWR fuels under accident conditions
Irradiation Test of Advanced PWR Fuel in Fuel Test Loop at HANARO