Influence of synthesis condition on product formation: hydrothermal auto-oxidated synthesis of five copper halides with ratio of Cu(I)/Cu(II) in 1:1, 2:1, 3:1, 4:1 and 1:0
- Department of Chemistry, Fuzhou University, Fuzhou, Fujian 350002 (China)
The hydrothermal synthesis and structural characterization of five copper iodides derived from chelated ligands, 1, 10-phenanthroline (phen), ethylenediamine (en) and 1, 3-propanediamine, are reported. Except monovalent copper compound 1 ((phen)Cu{sub 3}I{sub 3}1), other four compounds ([Cu(phen){sub 2}I][CuI{sub 2}] 2, [Cu(phen){sub 2}I][Cu{sub 3}I{sub 4}] 3, [Cu(en){sub 2}][Cu{sub 4}(phen){sub 2}I{sub 6}] 4 and [Cu(1, 3-propanediamine){sub 2}][CuI{sub 2}]{sub 2}5) are mixed-valent Cu(I)-Cu(II) compounds by partially auto-oxidated from Cu(I). Supramolecular frameworks of these compounds can be assembled by C/N-H...I hydrogen bonds, Cu(I)-Cu(I) interaction, weak Cu-I semicoordinate interaction, C-H...{pi} and {pi}-{pi} stacking interactions. It's noteworthy that we find hydrothermal synthesis under higher pH value, higher synthesis temperature and longer reaction time can obtain higher ratio of Cu(I)/Cu(II) copper iodides and organic ligand with lower steric hinderance is prone to coordinated with divalent copper to form cation unit. Finally, the fluorescent study shows 1 exhibits intense orange-red luminescence with long lifetime at 293 K and more intense emission and longer lifetime at 77 K. Moreover, the room temperature EPR spectra of above five compounds not only show the valence of copper but demonstrate the coordination environment of Cu(II) centre. - Graphical abstract: The influence of hydrothermal synthesis condition on the ratio of Cu(I)/Cu(II) of five copper iodides, with 1:0, 1:1, 3:1, 4:1, 2:1, respectively, is deduced and the rivalrousness of 1,10-phenanthroline, ethylenediamine and 1, 3-propanediamine is discussed as well. The fluorescent study shows 1 exhibits intense orange-red luminescence with long lifetime ({tau}=1.25 {mu}s) at 293 K and more intense emission and longer lifetime({tau}=6.95 {mu}s) at 77 K.
- OSTI ID:
- 21212141
- Journal Information:
- Journal of Solid State Chemistry, Vol. 181, Issue 12; Other Information: DOI: 10.1016/j.jssc.2008.09.011; PII: S0022-4596(08)00476-3; Copyright (c) 2008 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
X-ray photoelectron investigation of complex compounds of copper(II) with nitrogen-containing ligands
Synthesis, crystal structure and magnetic characterization of metal(II) coordination polymers based on 2-carboxyethylphosphonic acid and 1,10-phenanthroline (metal=Cu, Co, Cd)