Correlation of chemical composition and electrical properties of rf sputtered alumina films
- Institut fuer Physikalische und Theoretische Chemie der Universitaet, Bonn Wegelerstr. 12, 53115 Bonn (Germany)
Alumina films were prepared by radio frequency magnetron sputtering from an aluminum oxide target on an indium tin oxide covered glass. The purpose of the study was to test the influence of the sputter parameters on the elemental composition, surface morphology, and electrical insulation properties (breakdown fields and leakage currents). Tested parameters were the sputter gas (Ar) pressure, the sputter rate, the sputter power, the sputter gas composition (Ar:O{sub 2}), the conditioning of the target, the residual base pressure, and the substrate temperature. The surface morphology of the films was investigated by atomic force microscopy. Depth profiles of the elemental compositions were measured by elastic recoil detection using energetic heavy ions, and the insulation properties were investigated by current voltage measurements and impedance spectroscopy. The main finding is that the leakage currents increase by about five orders of magnitude, if the atomic ratio of O:Al increases from 1.35 to 2.0. In parallel the breakdown fields decrease by a factor of 100, and the character of the breakdowns changes from soft to hard. The highest breakdown fields (2.4 MV/cm) and smallest leakage currents (6.5x10{sup -8} A/cm{sup 2} at 2.0 MV/cm) are obtained for slightly Al rich films with small atomic concentrations of H (<0.5 at. %). These films were sputtered in pure Ar and under the lowest possible pressure of the residual gas.
- OSTI ID:
- 21195000
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Vol. 27, Issue 2; Other Information: DOI: 10.1116/1.3065978; (c) 2009 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
Gate quality Si{sub 3}N{sub 4} prepared by low temperature remote plasma enhanced chemical vapor deposition for III{endash}V semiconductor-based metal{endash}insulator{endash}semiconductor devices
Cuprous oxide--indium--tin oxide thin film photovoltaic cells