Cs{sub 4}P{sub 2}Se{sub 10}: A new compound discovered with the application of solid-state and high temperature NMR
- Department of Chemistry, Michigan State University, East Lansing, MI 48824 (United States)
The new compound Cs{sub 4}P{sub 2}Se{sub 10} was serendipitously produced in high purity during a high-temperature synthesis done in a nuclear magnetic resonance (NMR) spectrometer. {sup 31}P magic angle spinning (MAS) NMR of the products of the synthesis revealed that the dominant phosphorus-containing product had a chemical shift of -52.8 ppm that could not be assigned to any known compound. Deep reddish brown well-formed plate-like crystals were isolated from the NMR reaction ampoule and the structure was solved with X-ray diffraction. Cs{sub 4}P{sub 2}Se{sub 10} has the triclinic space group P-1 with a=7.3587(11) A, b=7.4546(11) A, c=10.1420(15) A, {alpha}=85.938(2){sup o}, {beta}=88.055(2){sup o}, and {gamma}=85.609(2){sup o} and contains the [P{sub 2}Se{sub 10}]{sup 4-} anion. To our knowledge, this is the first compound containing this anion that is composed of two tetrahedral (PSe{sub 4}) units connected by a diselenide linkage. It was also possible to form a glass by quenching the melt in ice water, and Cs{sub 4}P{sub 2}Se{sub 10} was recovered upon annealing. The static {sup 31}P NMR spectrum at 350 deg. C contained a single peak with a -35 ppm chemical shift and a {approx}7 ppm peak width. This study highlights the potential of solid-state and high-temperature NMR for aiding discovery of new compounds and for probing the species that exist at high temperature. - Graphical abstract: The new compound Cs{sub 4}P{sub 2}Se{sub 10} was discovered following a high-temperature in situ synthesis in the NMR spectrometer and the structure was determined by single-crystal X-ray diffraction. It contains the new [P{sub 2}Se{sub 10}]{sup 4-} anion.
- OSTI ID:
- 21049523
- Journal Information:
- Journal of Solid State Chemistry, Vol. 180, Issue 10; Other Information: DOI: 10.1016/j.jssc.2007.08.002; PII: S0022-4596(07)00314-3; Copyright (c) 2007 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Chemical disorder in non-oxide chalcogenide glasses. Site speciation in the system phosphorus-selenium by magic angle spinning NMR at very high spinning speeds
Reaction between CO/sub 2/ and phosphate to form carboxyphosphate