Development of Residual Stress Improvement for Nuclear Pressure Vessel Instrumentation Nozzle Weld Joint (P-43+P-8) by Means of Induction Heating
- Ishikawajima-Harima Heavy Industies Co., Ltd (Japan)
As a counter measurement of intergranular stress corrosion cracking (IGSCC) in boiling water reactors, the induction heating stress improvement (IHSI) has been developed as a method to improve the stress factor, especially residual stresses in affected areas of pipe joint welds. In this method, a pipe is heated from the outside by an induction coil and cooled from the inside with water simultaneously. By thermal stresses to produce a temperature differential between the inner and outer pipe surfaces, the residual stress inside the pipe is improved compression. IHSI had been applied to weld joints of austenitic stainless steel pipes (P-8+P-8). However IHSI had not been applied to weld joints of nickel-chromium-iron alloy (P-43) and austenitic stainless steel (P-8). This weld joint (P-43+P-8) is used for instrumentation nozzles in nuclear power plants' reactor pressure vessels. Therefore for the purpose of applying IHSI to this one, we studied the following: Investigation of IHSI conditions (Essential Variables); Residual stresses after IHSI; Mechanical properties after IHSI. This paper explains that IHSI is sufficiently effective in improvement of the residual stresses for this weld joint (P-43+P-8), and that IHSI does not cause negative effects by results of mechanical properties, and IHSI is verified concerning applying it to this kind of weld joint. (authors)
- Research Organization:
- The ASME Foundation, Inc., Three Park Avenue, New York, NY 10016-5990 (United States)
- OSTI ID:
- 20995425
- Resource Relation:
- Conference: 14. international conference on nuclear engineering (ICONE 14), Miami, FL (United States), 17-20 Jul 2006; Other Information: Country of input: France
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evaluation of stainless steel pipe cracking: causes and fixes
Qualification of induction heating stress improvement for mitigation of stress corrosion cracking