Intersubband absorption in CdSe/Zn{sub x}Cd{sub y}Mg{sub 1-x-y}Se self-assembled quantum dot multilayers
- Department of Electrical Engineering, City College of the City University of New York, New York, New York 10031 (United States)
The authors report the observation of intersubband absorption in multilayers of CdSe/Zn{sub x}Cd{sub y}Mg{sub 1-x-y}Se self-assembled quantum dots. The samples were grown by molecular beam epitaxy on InP substrates. For samples with the CdSe dot layers doped with Cl and with the deposited CdSe equivalent layer thickness between 5.2 and 6.9 ML, peak absorption between 2.5 and 3.5 {mu}m was observed. These materials are promising for intersubband devices operating in the mid- and near-infrared ranges.
- OSTI ID:
- 20971823
- Journal Information:
- Applied Physics Letters, Vol. 90, Issue 7; Other Information: DOI: 10.1063/1.2679783; (c) 2007 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ordering mechanism of stacked CdSe/ZnS{sub x}Se{sub 1-x} quantum dots: A combined reciprocal-space and real-space approach
Enhanced Emission from Bright Excitons in Asymmetrically Strained Colloidal CdSe/CdxZn1–xSe Quantum Dots
Codesigning Alloy Compositions of CdSe y Te 1− y Absorbers and Mg x Zn 1− x O Contacts to Increase Solar Cell Efficiency
Journal Article
·
Tue Nov 15 00:00:00 EST 2005
· Physical Review. B, Condensed Matter and Materials Physics
·
OSTI ID:20971823
+7 more
Enhanced Emission from Bright Excitons in Asymmetrically Strained Colloidal CdSe/CdxZn1–xSe Quantum Dots
Journal Article
·
Thu Sep 02 00:00:00 EDT 2021
· ACS Nano
·
OSTI ID:20971823
+3 more
Codesigning Alloy Compositions of CdSe y Te 1− y Absorbers and Mg x Zn 1− x O Contacts to Increase Solar Cell Efficiency
Journal Article
·
Wed Jul 20 00:00:00 EDT 2022
· Solar RRL
·
OSTI ID:20971823
+4 more