Synthesis of MgNb{sub 2}O{sub 6} by coprecipitation
Journal Article
·
· Materials Research Bulletin
- Physical and Materials Chemistry Division, National Chemical Laboratory, Pune 411008 (India)
- Center for Materials Characterization, National Chemical Laboratory, Pune 411008 (India)
A simple coprecipitation technique was used successfully to synthesize fine powders of MgNb{sub 2}O{sub 6} (MN) phase. An aqueous mixture of ammonium carbonate and ammonium hydroxide was used to precipitate Mg{sup 2+} and Nb{sup 5+} cations as carbonate and hydroxide respectively under basic conditions. This precipitate on heating at 750 deg. C produced MN powders. For comparison MN powders were prepared by the traditional solid state method. The phase content and the lattice parameters were studied by powder X-ray diffraction (XRD). Particle size and morphology of the particles were studied by scanning electron microscopy (SEM)
- OSTI ID:
- 20895240
- Journal Information:
- Materials Research Bulletin, Vol. 41, Issue 7; Other Information: DOI: 10.1016/j.materresbull.2005.12.009; PII: S0025-5408(06)00013-4; Copyright (c) 2006 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
A co-precipitation technique to prepare BiNbO{sub 4}, MgTiO{sub 3} and Mg{sub 4}Ta{sub 2}O{sub 9} powders
The low temperature synthesis and characterization of Bi{sub 3.25}La{sub 0.75}Ti{sub 3}O{sub 12} powder by hydroxide coprecipitation in aqueous medium
Solution synthesis and characterization of lithium manganese oxide cathode materials
Journal Article
·
Thu Feb 02 00:00:00 EST 2006
· Materials Research Bulletin
·
OSTI ID:20895240
+2 more
The low temperature synthesis and characterization of Bi{sub 3.25}La{sub 0.75}Ti{sub 3}O{sub 12} powder by hydroxide coprecipitation in aqueous medium
Journal Article
·
Mon Oct 04 00:00:00 EDT 2004
· Materials Research Bulletin
·
OSTI ID:20895240
Solution synthesis and characterization of lithium manganese oxide cathode materials
Conference
·
Sat Jul 01 00:00:00 EDT 1995
·
OSTI ID:20895240