Resistance of geopolymer materials to acid attack
This article presents an investigation into durability of geopolymer materials manufactured using a class F fly ash (FA) and alkaline activators when exposed to 5% solutions of acetic and sulfuric acids. The main parameters studied were the evolution of weight, compressive strength, products of degradation and microstructural changes. The degradation was studied using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The performance of geopolymer materials when exposed to acid solutions was superior to ordinary Portland cement (OPC) paste. However, significant degradation of strength was observed in some geopolymer materials prepared with sodium silicate and with a mixture of sodium hydroxide and potassium hydroxide as activators. The deterioration observed was connected to depolymerisation of the aluminosilicate polymers in acidic media and formation of zeolites, which in some cases lead to a significant loss of strength. The best performance was observed in the geopolymer material prepared with sodium hydroxide and cured at elevated temperature, which was attributed to a more stable cross-linked aluminosilicate polymer structure formed in this material.
- OSTI ID:
- 20702131
- Journal Information:
- Cement and Concrete Research, Vol. 35, Issue 4; Other Information: DOI: 10.1016/j.cemconres.2004.06.005; PII: S0008884604002595; Copyright (c) 2004 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Geopolymeric materials prepared using Class F fly ash and elevated temperature curing
Preparation and characterization of a hybrid alkaline binder based on a fly ash with no commercial value