Crystallographic variant selection in {alpha}-{beta} brass
Journal Article
·
· Acta Materialia
- Manchester Materials Science Centre, University of Manchester, Grosvenor Street, Manchester M1 7HS (United Kingdom)
The transformation texture of {alpha}/{beta} brass with a diffusional Widmanstaetten {alpha} growth morphology has been investigated. Electron micrographs and electron backscattered diffraction was used to determine that the orientation relationship between the {beta} phase and the {alpha} associated with nucleation at {beta} grain boundaries was 44.3 deg <1 1 6>. Crystallographic variant selection was observed across those prior {beta}/{beta} grain boundaries, but this has little effect on the transformation texture due to the crystal symmetry. The effect of the crystallographic variant selection on texture is further weakened by nucleation of diffusional transformed {alpha} in the grain interior.
- OSTI ID:
- 20637147
- Journal Information:
- Acta Materialia, Vol. 53, Issue 3; Other Information: DOI: 10.1016/j.actamat.2004.10.043; PII: S1359-6454(04)00656-1; Copyright (c) 2004 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 1359-6454
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystallographic variant selection in Ti-6Al-4V
Variant selection in transformation texture from the {beta} to {alpha} phase in Cu-40 mass% Zn alloy
Variant selection in {alpha} {yields} {beta} {yields} {alpha} phase transformation of cold rolled titanium sheet
Journal Article
·
Mon Oct 04 00:00:00 EDT 2004
· Acta Materialia
·
OSTI ID:20637147
Variant selection in transformation texture from the {beta} to {alpha} phase in Cu-40 mass% Zn alloy
Journal Article
·
Fri Apr 23 00:00:00 EDT 1999
· Acta Materialia
·
OSTI ID:20637147
Variant selection in {alpha} {yields} {beta} {yields} {alpha} phase transformation of cold rolled titanium sheet
Journal Article
·
Mon Apr 15 00:00:00 EDT 1996
· Scripta Materialia
·
OSTI ID:20637147