Light-induced metastable defects or light-induced metastable H atoms in a-Si:H films?
In hydrogenated amorphous silicon (a-Si:H) films, the increase of the metastable defect density under high-intensity illumination is usually described by an empirical two-parameter stretched-exponential time dependence (characteristic time {tau}{sub SE} and dispersion parameter {beta}). In this study, a clearly different (one-parameter) analytic function is obtained from a microscopic model based on the formation of metastable H (MSH) atoms in a-Si:H films. Assuming that MSH atoms are the only mobile species, only three chemical reactions are significant: MSH are produced from doubly hydrogenated (SiH HSi) configurations and trapped either at broken bonds or Si-H bonds, corresponding respectively to light-induced annealing (LIA) and light-induced creation (LIC) of defects. Competition between trapping sites results in a saturation of N(t) at a steady-state value N{sub ss}. A one-parameter fit of this analytical function to experimental data is generally good, indicating that the use of a statistical distribution of trap energies is not necessary.
- Research Organization:
- Ecole Polytechnique, Palaiseau (FR)
- OSTI ID:
- 20085464
- Resource Relation:
- Conference: Amorphous and Microcrystalline Silicon Technology - 1997, San Francisco, CA (US), 03/31/1997--04/04/1997; Other Information: PBD: 1997; Related Information: In: Amorphous and microcrystalline silicon technology--1997. Materials Research Society symposium proceedings, Volume 467, by Wagner, S.; Hack, M.; Schiff, E.A.; Schropp, R.; Shimizu, I. [eds.], 999 pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Light induced effects in a-Si:H films alloyed with sulfur
Metastable defects in a-Si:H from bond-length disorder