Influence of overaging treatment on localized corrosion of Al 6056
The influence of T78 overaging treatment on the corrosion behavior of AL 6056 (UNS A96056) in 1 M sodium chloride (NaCl) solution was investigated. The overaged alloy presented the same localized corrosion mechanisms as Al 6056-T6. However, Al 6056-T78 coarse intermetallic Al-Mg-Si-containing particles were found to be more reactive than those in the Al 6056-T6 alloy and were nucleation sites for pits. Pitting and intergranular corrosion were dependent upon each other; intergranular corrosion nucleated on pit walls. A quantitative study showed that T78 overaging of Al 6056 offered a better resistance to intergranular corrosion compared to T6 peak-aging treatment. The overaged alloy will be able to replace the traditional Al 2024 because of the efficiency of this overaging treatment.
- Research Organization:
- UPRESA CNRS, Toulouse (FR)
- OSTI ID:
- 20014467
- Journal Information:
- Corrosion (Houston), Vol. 56, Issue 1; Other Information: PBD: Jan 2000; ISSN 0010-9312
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion protection of high-copper aluminum alloys using green technology
Corrosion behavior of aluminum-lithium alloys