Experiments on fracture toughness of thick-wall cylinder for modes I, II, III
Conference
·
OSTI ID:20014209
There have been few data on fracture toughness for Mode 2 and 3 as compared with those for Mode 1. Experimental data on fracture toughness of plates made of ductile cast iron (ASTM A874-89) and forged steel (ASME SA350 LF5 C1.1) were obtained at a temperature range from 77K to 293K for Mode 1, 2 and 3. The results showed: J{sub IC} < J{sub IIC} < J{sub IIIC}, and K{sub IC} < K{sub IIC} K{sub IIIC}. Integrity of a thick-wall cylinder with artificial flaw was demonstrated against brittle fracture at 233K for Mode 1, 2 and 3, which is one of the design requirements of containers shipping radioactive materials.
- Research Organization:
- CRIEPI, Abiko (JP)
- OSTI ID:
- 20014209
- Resource Relation:
- Conference: 1999 TMS Fall Meeting, Julia R. Weertman Symposium: Advanced Materials for the 21st Century, Cincinnati, OH (US), 10/31/1999--11/04/1999; Other Information: PBD: 1999; Related Information: In: Advanced materials for the 21st century: The 1999 Julia R. Weertman symposium, by Chung, Y.W.; Dunand, D.C.; Liaw, P.K.; Olson, G.B. [eds.], 585 pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of loading mode on the fracture toughness of a ferritic/martensitic stainless steel
Fracture toughness of ferritic materials in light water nuclear reactor vessels. Final report
Effect of loading mode on the fracture toughness of a reduced activation ferritic/martensitic stainless steel
Journal Article
·
Fri Sep 01 00:00:00 EDT 1995
· Metallurgical Transactions, A
·
OSTI ID:20014209
+1 more
Fracture toughness of ferritic materials in light water nuclear reactor vessels. Final report
Technical Report
·
Mon Oct 13 00:00:00 EDT 1975
·
OSTI ID:20014209
+1 more
Effect of loading mode on the fracture toughness of a reduced activation ferritic/martensitic stainless steel
Conference
·
Wed Sep 01 00:00:00 EDT 1993
·
OSTI ID:20014209
+1 more