Influence of nitrogen in the shielding gas on corrosion resistance of duplex stainless steel welds
The influence of nitrogen in shielding gas on the corrosion resistance of welds of a duplex stainless steel (grade U-50), obtained by gas tungsten arc (GTA) with filler wire, autogenous GTA (bead-on-plate), electron beam welding (EBW), and microplasma techniques, has been evaluated in chloride solutions at 30 C. Pitting attack has been observed in GTA, electron beam welding, and microplasma welds when welding has been carried out using pure argon as the shielding gas. Gas tungsten arc welding with 5 to 10% nitrogen and 90 to 95% argon, as the shielding gas, has been found to result in an improved pitting corrosion resistance of the weldments of this steel. However, the resistance of pitting of autogenous welds (bead-on-plate) obtained in pure argon as the shielding gas has been observed to remain unaffected. Microscopic examination, electron probe microanalysis (EPMA), and x-ray diffraction studies have revealed that the presence of nitrogen in the shielding gas in the GTA welds not only modifies the microstructure and the austenite to ferrite ratio but also results in a nearly uniform distribution of the various alloying elements, for example, chromium, nickel, and molybdenum among the constituent phases, which are responsible for improved resistance to pitting corrosion.
- Research Organization:
- BARC, Tarapur (IN)
- OSTI ID:
- 20000467
- Journal Information:
- Journal of Materials Engineering and Performance, Vol. 8, Issue 5; Other Information: PBD: Oct 1999; ISSN 1059-9495
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of shielding gas hydrogen content on the arc behavior in gas tungsten arc welding
Evaluation of pitting corrosion resistance of high-alloyed stainless steels welds for FGD plants in Korea