Diffusive and inelastic scattering in ballistic-electron-emission spectroscopy and ballistic-electron-emission microscopy
- Rensselaer Polytechnic Institute, Troy, NY (United States); and others
Ballistic-electron-emission microscopy (BEEM) of Au/Si(001) n type was done to study whether elastic scattering in the Au overlayer is dominant. It was found that there is no dependence of the BEEM current on the relative gradient of the Au surface with respect to the Si interface, and this demonstrates that significant elastic scattering must occur in the Au overlayer. Ballistic-electron-emission spectroscopy (BEES) was also done, and, rather than using the conventional direct-current BEES, alternating-current (ac) BEES was done on Au/Si and also on Au/PtSi/Si(001) n type. The technique of ac BEES was found to give linear threshold for the Schottky barrier, and it also clearly showed the onset of electron-hole pair creation and other inelastic scattering events. The study of device quality PtSi in Au/PtSi/Si(001) yielded an attenuation length of 4 nm for electrons of energy 1 eV above the PtSi Fermi energy. 20 refs., 5 figs.
- OSTI ID:
- 161737
- Report Number(s):
- CONF-930115-; ISSN 0734-211X; CNN: Contract N0014-92-J-1277; Contract F19628-91-K-0030; TRN: 95:004881-0057
- Journal Information:
- Journal of Vacuum Science and Technology. B, Microelectronics Processing and Phenomena, Vol. 11, Issue 4; Conference: 20. physics and chemistry of semiconductor interfaces, Williamsburg, VA (United States), 25-29 Jan 1993; Other Information: PBD: Jul-Aug 1993
- Country of Publication:
- United States
- Language:
- English
Similar Records
Schottky barrier height measurements of Cu/Si(001), Ag/Si(001), and Au/Si(001) interfaces utilizing ballistic electron emission microscopy and ballistic hole emission microscopy
Ballistic-electron emission microscopy at metal/GaP(110) interfaces: Electron transport and Schottky-barrier heights