Beam Damage of Poly(Vinyl Chloride) [PVC] Film as Observed by X-ray Photoelectron Spectroscopy
Journal Article
·
· Surface Science Spectra
XPS spectra of a spin-coated film poly(vinyl chloride) (PVC) were collected over a period of 243 minutes at 303 K to determine specimen damage during long exposures to monochromatic Al Ka x-rays. For this PVC film we measured the loss of chlorine as a function of time by rastering a focused 104.6 w 100 um diameter x-ray beam over a 1.4 mm x 0.2 mm area on the sample.
- Research Organization:
- Pacific Northwest National Lab., Richland, WA (US), Environmental Molecular Sciences Laboratory (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 15016101
- Report Number(s):
- PNWD-SA-6564; SSSPEN; 3423; KP1301030; TRN: US0501851
- Journal Information:
- Surface Science Spectra, Vol. 10, Issue 101; Other Information: PBD: 8 Mar 2003; ISSN 1055-5269
- Country of Publication:
- United States
- Language:
- English
Similar Records
Beam damage of poly(vinyl chloride) [PVC] as observed by x-ray photoelectron spectroscopy at 143 K, 303 K and 373 K.
Beam Damage of HS (CH2)15 COOH Terminated Self Assembled Monolayer (SAM) as Observed by X-Ray Photoelectron Spectroscopy
Electron Beam Damage in Poly(Vinyl Chloride) and Poly(Acrylonitrile) as Observed by Auger Electron Spectroscopy
Journal Article
·
Sat Mar 08 00:00:00 EST 2003
· Surface Science Spectra
·
OSTI ID:15016101
Beam Damage of HS (CH2)15 COOH Terminated Self Assembled Monolayer (SAM) as Observed by X-Ray Photoelectron Spectroscopy
Journal Article
·
Tue Oct 25 00:00:00 EDT 2011
· Surface Science Spectra
·
OSTI ID:15016101
Electron Beam Damage in Poly(Vinyl Chloride) and Poly(Acrylonitrile) as Observed by Auger Electron Spectroscopy
Journal Article
·
Fri Mar 07 00:00:00 EST 2003
· Surface Science Spectra
·
OSTI ID:15016101