Title: Tuning Thermoelectric Properties of Type I Clathrate K 8–x Ba x Al 8+x Si 38–x through Barium Substitution

The thermal stability and thermoelectric properties of type I clathrate K8Al8Si38 up to 873 K are reported. K8Al8Si38 possesses a high absolute Seebeck coefficient value and high electrical resistivity in the temperature range of 323 to 873 K, which is consistent with previously reported low temperature thermoelectric properties. Samples with Ba partial substitution at the K guest atom sites were synthesized from metal hydride precursors. The samples with the nominal chemical formula of K8–xBaxAl8+xSi38–x (x = 1, 1.5, 2) possess type I clathrate structure (cubic, Pm3n), confirmed by X-ray diffraction. The guest atom site occupancies and thermal motions were investigated with Rietveld refinement of synchrotron powder X-ray diffraction. Transport properties of Ba-containing samples were characterized from 2 to 300 K. The K–Ba alloy phases showed low thermal conductivity and improved electrical conductivity compared to K8Al8Si38. Electrical resistivity and Seebeck coefficients were measured over the temperature range of 323 to 873 K. Thermal conductivity from 323 to 873 K was estimated from the Wiedemann–Franz relation and lattice thermal conductivity extrapolation from 300 to 873 K. K8–xBaxAl8+xSi38–x (x = 1, 1.5) synthesized with Al deficiency showed enhanced electrical conductivity, and the absolute Seebeck coefficients decrease with the increased carrier concentration. When xmore » = 2, the Al content increases toward the electron balanced composition, and the electrical resistivity increases with the decreasing charge carrier concentration. Overall, K6.5Ba1.5Al9Si37 achieves an enhanced zT of 0.4 at 873 K.« less
Publication Date:
OSTI Identifier:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Chemistry of Materials; Journal Volume: 28; Journal Issue: 9
American Chemical Society (ACS)
Research Org:
Advanced Photon Source (APS), Argonne National Laboratory (ANL), Argonne, IL (US)
Sponsoring Org:
USDOE Office of Science (SC), Basic Energy Sciences (BES) (SC-22)
Country of Publication:
United States