Influence of microstructure on the corrosion resistance of AISI type 304L and type 316L sintered stainless steels exposed to ferric chloride solution
Journal Article
·
· Materials Characterization
- Univ. Complutense, Madrid (Spain). Dept. of Materials Sciences
- Pontificia Univ. Catolica del Peru, Lima (Peru). Corrosion Lab.
The corrosion behavior of type 304L and type 316L austenitic stainless steels, produced by powder metallurgy, when exposed to a ferric chloride solution was studied. The exposures were conducted according to ASTM G48-76, Method A. The influence of ferric chloride concentration and exposure temperature on the corrosion kinetics of these materials was evaluated. A mechanism is proposed to explain the associated morphology observed in the microstructures produced after exposure of these P/M alloys to the aggressive medium.
- OSTI ID:
- 131422
- Journal Information:
- Materials Characterization, Vol. 35, Issue 3; Other Information: PBD: Oct 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of pH and chloride concentration on the pitting and crevice corrosion behavior of high-alloy stainless steels
Cold Spray Deposition of 304L Stainless Steel to Mitigate Chloride-Induced Stress Corrosion Cracking in Canisters for Used Nuclear Fuel Storage
Accelerated corrosion testing of cold spray coatings on 304L in chloride environments
Journal Article
·
Sat Apr 01 00:00:00 EST 2000
· Corrosion (Houston)
·
OSTI ID:131422
+3 more
Cold Spray Deposition of 304L Stainless Steel to Mitigate Chloride-Induced Stress Corrosion Cracking in Canisters for Used Nuclear Fuel Storage
Journal Article
·
Tue Sep 01 00:00:00 EDT 2020
· Journal of Nuclear Materials
·
OSTI ID:131422
+3 more
Accelerated corrosion testing of cold spray coatings on 304L in chloride environments
Journal Article
·
Thu Nov 17 00:00:00 EST 2022
· Frontiers in Metals and Alloys
·
OSTI ID:131422
+2 more