First-principles insights into the nature of zirconium–iodine interactions and the initiation of iodine-induced stress–corrosion cracking
Journal Article
·
· Journal of Nuclear Materials
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1252387
- Journal Information:
- Journal of Nuclear Materials, Journal Name: Journal of Nuclear Materials Vol. 458 Journal Issue: C; ISSN 0022-3115
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- Netherlands
- Language:
- English
Cited by: 18 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Influence of surface condition on crack initiation in iodine-induced stress corrosion cracking of zircaloys
Advanced 3D characterisation of iodine induced stress corrosion cracks in zirconium alloys
Stress-corrosion cracking (SCC) as a result of pellet-clad chemical interaction (PCCI): Focus on initiation by iodine
Journal Article
·
Tue Dec 01 00:00:00 EST 1981
· Nucl. Technol.; (United States)
·
OSTI ID:1252387
Advanced 3D characterisation of iodine induced stress corrosion cracks in zirconium alloys
Journal Article
·
Sun Jul 15 00:00:00 EDT 2018
· Materials Characterization
·
OSTI ID:1252387
+5 more
Stress-corrosion cracking (SCC) as a result of pellet-clad chemical interaction (PCCI): Focus on initiation by iodine
Conference
·
Tue Jun 05 00:00:00 EDT 2012
·
OSTI ID:1252387
+3 more