Title: An evaluation of the Johnson-Cook model to simulate puncture of 7075 aluminum plates.

The objective of this project was to evaluate the use of the Johnson-Cook strength and failure models in an adiabatic finite element model to simulate the puncture of 7075- T651 aluminum plates that were studied as part of an ASC L2 milestone by Corona et al (2012). The Johnson-Cook model parameters were determined from material test data. The results show a marked improvement, in particular in the calculated threshold velocity between no puncture and puncture, over those obtained in 2012. The threshold velocity calculated using a baseline model is just 4% higher than the mean value determined from experiment, in contrast to 60% in the 2012 predictions. Sensitivity studies showed that the threshold velocity predictions were improved by calibrating the relations between the equivalent plastic strain at failure and stress triaxiality, strain rate and temperature, as well as by the inclusion of adiabatic heating.
Publication Date:
OSTI Identifier:
Report Number(s):
DOE Contract Number:
Resource Type:
Technical Report
Research Org:
Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)
Sponsoring Org:
USDOE National Nuclear Security Administration (NNSA)
Country of Publication:
United States