Title: Enhanced Performance of Li|LiFePO4 Cells Using CsPF6 as an Electrolyte Additive

The practical application of lithium (Li) metal anode in rechargeable Li batteries is hindered by both the growth of Li dendrites and the low Coulombic efficiency (CE) during repeated charge/discharge cycles. Recently, we have discovered that CsPF6 as an electrolyte additive can significantly suppress Li dendrite growth and lead to highly compacted and well aligned Li nanorod structure during Li deposition on copper substrates. In this paper, the effect of CsPF6 additive on the performance of rechargeable Li metal batteries with lithium iron phosphate (LFP) cathode was further studied. Li|LFP coin cells with CsPF6 additive in electrolytes show well protected Li anode surface, decreased resistance, enhanced rate capability and extended cycling stability. In Li|LFP cells, the electrolyte with CsPF6 additive shows excellent long-term cycling stability (at least 500 cycles) at a charge current density of 0.5 mA cm-2 without internal short circuit. At high charge current densities, the effect of CsPF6 additive becomes less significant. Future work needs to be done to protect Li metal anode, especially at high charge current densities and for long cycle life.
; ; ; ; ; ; ;
Publication Date:
OSTI Identifier:
Report Number(s):
48379; VT1201000
DOE Contract Number:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Power Sources, 293:1062-1067
Research Org:
Pacific Northwest National Laboratory (PNNL), Richland, WA (US), Environmental Molecular Sciences Laboratory (EMSL)
Sponsoring Org:
Country of Publication:
United States
Environmental Molecular Sciences Laboratory