Final Report on MEGAPIE Target Irradiation and Post-Irradiation Examination

Technical Report · Tue Jun 30 00:00:00 EDT 2015

DOI:https://doi.org/10.2172/1188406· OSTI ID:1188406

Yong, Dai ^[1]

---

1. Paul Scherrer-Institut (Switzerland)

Megawatt pilot experiment (MEGAPIE) was successfully performed in 2006. One of the important goals of MEGAPIE is to understand the behaviour of structural materials of the target components exposed to high fluxes of high-energy protons and spallation neutrons in flowing LBE (liquid lead-bismuth eutectic) environment by conducting post-irradiation examination (PIE). The PIE includes four major parts: non-destructive test, radiochemical analysis of production and distribution of radionuclides produced by spallation reaction in LBE, analysis of LBE corrosion effects on structural materials, T91 and SS 316L steels, and mechanical testing of the T91 and SS 316L steels irradiated in the lower part of the target. The non-destructive test (NDT) including visual inspection and ultrasonic measurement was performed in the proton beam window area of the T91 calotte of the LBE container, the most intensively irradiated part of the MEGAPIE target. The visual inspection showed no visible failure and the ultrasonic measurement demonstrated no detectable change in thickness in the beam window area. Gamma mapping was also performed in the proton beam window area of the AlMg₃ safety-container. The gamma mapping results were used to evaluate the accumulated proton fluence distribution profile, the input data for determining irradiation parameters. Radiochemical analysis of radionuclides produced by spallation reaction in LBE is to improve the understanding of the production and distribution of radionuclides in the target. The results demonstrate that the radionuclides of noble metals, ²⁰⁷Bi, ¹⁹⁴Hg/Au are rather homogeneously distributed within the target, while radionuclides of electropositive elements are found to be deposited on the steel-LBE interface. The corrosion effect of LBE on the structural components under intensive irradiation was investigated by metallography. The results show that no evident corrosion damages. However, unexpected deep cracks were found in the EBW (electron beam weld) of the LBE container in the intensive irradiation zone of the target, which should be formed during irradiation. In the SS 316L steel of the flow guide tube, inclusions or precipitates enriched with O, Si, S, Ca, Ti and Mn were observed. Many of them are very long, up to a few mm, and located on grain boundaries along the extrusion direction of the tube. The degradation of the mechanical properties of the T91 and SS 316L steels has been investigated by conducting tensile tests on the specimens extracted from the T91 and SS 316L components in the intensive irradiation region. The results obtained from the proton beam window of the T91 calotte exhibit a good ductility of T91 steel after irradiation at 6-7 dpa (displacement per atom) in contact with flowing LBE.

• Research Organization: Paul Scherrer-Institut (Switzerland)
• Sponsoring Organization: USDOE Office of Nuclear Energy (NE)
• DOE Contract Number: NE0000652
• OSTI ID: 1188406
• Report Number(s): NE0000652
• Country of Publication: United States
• Language: English