A Qualitative Comparison of the C-Ring Test and the Jones Test as Standard Practice Test Methods for Studying Stress Corrosion Cracking in Ferritic Steels
- ORNL
Creep-strength-enhanced-ferritic (CSEF) steels have been widely implemented as water wall alloy materials in the coal-fired power industry for many years. The stress corrosion cracking (SCC) behavior of this class of materials is currently of significant interest to the industry due to recent failures. To better understand the test methods used to characterize SCC behavior in the laboratory, three representative CSEF alloys (T23, T24, and T92) were subjected to two SCC test protocols: the Jones Test set forth in DIN 50915, and the C-ring SCC test set forth in ASTM G38-01. Samples were tested in either the as-received (normalized + tempered) condition or in the normalized condition (quenched from 1065 C). Samples were exposed to aerated water in one test case and de-aerated water in a second test case for a period of 7 days at 200 C. It was found that for both test protocols, the normalized condition with aerated water led to severe cracking for all three alloys, whereas no evidence of cracking was found for the other conditions.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- FE USDOE - Office of Fossil Energy (FE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1185684
- Resource Relation:
- Conference: NACE Corrosion 2015, Dallas, TX, USA, 20150315, 20150319
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion and Stress Corrosion Cracking of High Cr Ferritic-Martensitic Steels in Supercritical Water
Effect of dissolved oxygen level on stress corrosion cracking susceptibility of structural steels