Composite Poly(vinylidene fluoride)/Polystyrene Latex Particles for Confined Crystallization in 180 nm Nanospheres via Emulsifier-Free Batch Seeded Emulsion Polymerization
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1162492
- Report Number(s):
- BNL-106436-2014-JA
- Journal Information:
- Macromolecules, Vol. 47, Issue 8; ISSN 0024--9297
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystal Orientation and Temperature Effects on Double Hysteresis Loop Behavior in a Poly(vinylidene fluoride-co-trifluoroethylene-co-chlorotrifluoroethylene)-graft-Polystyrene Graft Copolymer
Emulsifier-free emulsion polymerization of tetrafluoroethylene by radiation. V. Effect of reaction conditions on the stability of polytetrafluoroethylene latex
Characterization of film formation from direct mini-emulsified polystyrene latex particles via SANS
Journal Article
·
Sun Dec 01 00:00:00 EST 2013
· Macromolecules
·
OSTI ID:1162492
+1 more
Emulsifier-free emulsion polymerization of tetrafluoroethylene by radiation. V. Effect of reaction conditions on the stability of polytetrafluoroethylene latex
Journal Article
·
Thu Feb 01 00:00:00 EST 1979
· J. Polym. Sci., Polym. Chem. Ed.; (United States)
·
OSTI ID:1162492
+1 more
Characterization of film formation from direct mini-emulsified polystyrene latex particles via SANS
Journal Article
·
Mon Aug 16 00:00:00 EDT 1993
· Macromolecules; (United States)
·
OSTI ID:1162492
+1 more