Unprecedented CO2-promoted hydrogen permeation in Ni-BaZr0.1Ce0.7Y0.1Yb0.1O3-δ membrane
Journal Article
·
· ACS Appl. Mater. Interfaces
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Heterogeneous Functional Materials Center (HeteroFoaM)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- SC0001061
- OSTI ID:
- 1160979
- Journal Information:
- ACS Appl. Mater. Interfaces, Related Information: HeteroFoaM partners with University of South Carolina (lead); University of California, Santa Barbara; University of Connecticut; Georgia Institute of Technology; Princeton University; Rochester Institute of Technology; Savannah River National Laboratory; University of South Carolina; University of Utah
- Country of Publication:
- United States
- Language:
- English
Similar Records
Unprecedented CO 2 -Promoted Hydrogen Permeation in Ni-BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ Membrane
The role of partial crystallinity on hydrogen permeation in Fe-Ni-B-Mo based metallic glass membranes
The role of partial crystallinity on hydrogen permeation in Fe–Ni–B–Mo based metallic glass membranes
Journal Article
·
Thu Dec 19 00:00:00 EST 2013
· ACS Applied Materials and Interfaces
·
OSTI ID:1160979
The role of partial crystallinity on hydrogen permeation in Fe-Ni-B-Mo based metallic glass membranes
Journal Article
·
· Journal of Membrane Science
·
OSTI ID:1160979
+3 more
The role of partial crystallinity on hydrogen permeation in Fe–Ni–B–Mo based metallic glass membranes
Journal Article
·
Mon Aug 01 00:00:00 EDT 2011
· Journal of Membrane Science
·
OSTI ID:1160979
+3 more