Title: Final Technical Report

The objective of this project is to develop a MgB2 superconducting RF (SRF) cavity technology. Compared to the currently-used SRF material niobium, MgB2 has a much higher Tc of 40 K, a lower residual resistivity (< 0.1 µΩcm), and a higher thermodynamic critical field Hc. SRF cavities with MgB2 coatings have the potentials for higher Q, higher gradient, and higher operation temperatures. A MgB2 SRF technology can significantly reduce the operating costs of particle accelerators when these potentials are realized. In this project, we have made significant progresses in the deposition of large-area (2” diameter) MgB2 films for RF characterizations, deposition of MgB2 films on metal substrates including Nb, Mo, Ta, and stainless steel, enhancement of Hc1 with decreasing MgB2 film thickness, fabrication and characterization of MgB2/MgO multilayers, and deposition of MgB2 films of excellent superconducting properties on the wall of a 6-GHz RF cavity. These results have laid foundation for a MgB2 superconducting SRF cavity technology.
Publication Date:
OSTI Identifier:
Report Number(s):
DOE Contract Number:
Resource Type:
Technical Report
Research Org:
Temple University
Sponsoring Org:
USDOE; USDOE Office of Science (SC), High Energy Physics (HEP) (SC-25)
Country of Publication:
United States
Superconducting Radio Frequency Cavities