Sintering of corundum ceramics based on aluminum hydroxide
- D.I. Mendeleev Russian Chemical Technological Univ., Novomoskovsk (Russian Federation)
The possibility of using aluminum hydroxide obtained by the precipitation method for synthesis of corundum ceramics with additives forming a liquid phase during firing and without additives, is investigated. The optimum parameters of the manufacturing process and the main properties of the material recommended for testing in the production of glass ceramic substrates for integrated circuits are investigated.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 114994
- Journal Information:
- Glass and Ceramics, Vol. 52, Issue 1-2; Other Information: PBD: Sep 1995; TN: Translated from Steklo i Keramika; Nos. 1-2, 24-26(Jan-Feb 1995)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corundum ceramics with a low sintering temperature
Development of a corundum ceramic having a low sintering temperature
Effect of flux-forming additives on the sintering temperature and the properties of a corundum-based ceramic
Journal Article
·
Mon May 01 00:00:00 EDT 1995
· Refractories
·
OSTI ID:114994
Development of a corundum ceramic having a low sintering temperature
Journal Article
·
Mon Sep 01 00:00:00 EDT 1986
· Refractories (Engl. Transl.); (United States)
·
OSTI ID:114994
+1 more
Effect of flux-forming additives on the sintering temperature and the properties of a corundum-based ceramic
Journal Article
·
Sun Mar 01 00:00:00 EST 1987
· Refractories (Engl. Transl.); (United States)
·
OSTI ID:114994